LOCTITE SF 7460 - 1L EGFD (Podkład poliuretanowy)

LOCTITE SF 7460 - 1L EGFD (Podkład poliuretanowy) (IDH.2230716)

Product description:
LOCTITE SF 7460 is a one component, solvent, polyurethane based primer. It is designed to prime metal or concrete surfaces before polyurea coating products like Loctite PC 7280 or Loctite PC 7282. It is also used to prime existing polyurea coating for repairs or recoat time greater than 8 hours. This product hardens in thin layers by absorbing the humidity from the air or from the substrate in thecase of concrete. This wear and impact resistant film is visible under UV light. Further information about the product: biuro@woronko-kleje.pl

Directions for use:
Surface Preparation:
1. Remove dirt, oil, grease etc with a suitable cleaner, e.g. high pressure water cleaning system using LOCTITE SF 7840 or Loctite Natural Blue cleaner/degreaser.
2. All skip welds, weld splatter, buckshot, and other surface roughness must be ground down and smoothed; undercuts and pinholes must be ground smooth and filled. All projections, sharp edges, high points and fillets must be ground smooth to a radius of at least 3 mm (metal) and 6 mm (concrete) and all corners must be likewise rounded to maximize product performance.
3. Blast all surfaces to be coated with a sharp edged angular grit to a depth of profile of ≥60 microns ( mils),and a degree of cleanliness of Near White Metal (SIS SA 2½ /SSPC-SP 10). For immersion service, a degree ofcleanliness of White Metal (SIS SA 3/SSPC-SP 5) is required.
4. After blasting, metal surfaces should be cleaned, e.g. with LOCTITE SF 7063 or Loctite ODC Free Cleanerand Degreaser, and be coated before any oxidation or contamination takes place.
5. Metal that has been in contact with salt solutions, e.g. seawater, should be grit blasted and high-pressure water blasted, left for 24 hours to allow any salts in the metal to sweat to the surface. A test for chloride contamination should be performed.

Application:
● Ambient and substrate temperature range: 5 to 35 °C.
● Relative humidity: <98 %; substrate temperature must always be 3 °C higher than the dew point.
● Ideal product application is to use roller or air pressure / airless spray. The compressed air needs to be free of oil and water.
● Minimum film thickness per coat: 30 to 100 µm.
● This primer must be tack free before applying the coating Loctite PC 7280 or Loctite PC 7282.
● Maximum recoat time is 48 hours.

Storage:
Store product in the unopened container in a dry location. Material removed from containers may be contaminated during use. Do not return liquid to original container. Storage information may be indicated on the product container labeling. Optimal Storage: 10 °C to 30 °C. Storage below 10 °C or greater than 30 °C can adversely affect product properties. Henkel cannot assume responsibility for product which has been contaminated or stored under conditions other than those recommended.

Parameters:
  • Pot life at 23 °C, hours : 12
  • Tack Free Time @ °C, minutes:
    -Steel : 1
    -Concrete : 0.2 to 1
  • Recoat Time, hours:
    -Steel : <48
    -Concrete : <72
  • Residual Moisture, % : 8 to 10

    Full technical information can be found in the technical data sheet.