Product description:
TEROSON EP 5065 is a solvent free, two component adhesive, based on Epoxy resins. It has high final strength both at high and low temperatures (-40°C - 80°C). Curing can be obtained with both low and high temperature. The cured adhesive film is hard, but not brittle.
Application Areas:
TEROSON EP 5065 is mainly used in car repair for structural bonding of metals when requirements in terms of crash behaviors are high (e.g., car body steel with or without e-coat, galvanized steel and aluminum). Coated surfaces are protected against corrosion. Curing can take place at room temperature or be accelerated by the use of additional heat, e.g. IR radiator. The assembly bonded shall be designed so that the bonded surface or seams are only subjected to tensile or shear forces, but not to peel forces. It is recommended that bonding should be done with single overlaps. Uncured adhesive can be spot-welded. Further information about the product: biuro@woronko-kleje.pl
Directions for use:
Pretreatment:
The substrate should be dry, free from dust, oil, grease and other contaminants. An improvement of the adhesion can be achieved by grindings or sandblasting of the surface.
Application:
TEROSON EP 5065 is processed from a 2:1 cartridge. Only use cartridge pistols that are equipped with a piston rod. During the storage time and shipment a crystallization of the resin may occur. By heating the adhesive above 60 °C for about 60 minutes this physical process is reversible. All properties stay afterwards on the same level. It is recommended that the adhesive should be used with a minimum temperature of 15 °C. Prior to screwing the static mixer, a small amount of the material should be pressed out to ensure that both components are passed on simultaneously. Now, the static mixer is screwed onto it. To ensure proper mixing, discard the first approx. 4 cm of the adhesive bead. After mixing, the adhesive is ready for use and must be processed within 1 hour, since viscosity increases when curing starts. The processing time depends on the temperature. In order to avoid the bonded parts being displaced, it is recommended that they should always be fixed.
Curing:
The bonded parts, which have been fixed by means of a slight pressure applied to them, can be cured at room temperature or higher. They can be painted over after having reached their final strength. If suitable equipment for curing at higher temperature (infrared radiator, paint cabin that can be heated to 40 – 80 °C or other equipment) is available, this should always be givenpreference over curing at room temperature for the following reasons:
- Shorter curing time; further processing or treatment is possible after only 2 hours approx.
- Higher strength is achieved
- Higher resistance of the adhesive bond against chemical loads
Cleaning:
Fresh, uncured material can be removed with TEROSON VR 10. Cured adhesive can only be removed mechanically.
Storage:
Frost sensitive: under certain conditions (may cristalize, reversible at 60 °C) Recommended storage temperature : 15 to 35 °C Shelf life : 12 months in original packaging
Parameters:
Part A: Base : epoxy resin Colour : black Density : approx. 1.1 g/ml Viscosity : approx. 23 Pa.s Measuring equipment : Physica MCR 301 Measuring system : plate/plate Ø 20 mm Cross head peel speed : 10 s^(-1) Temperature : 23 °C
Part B:
Base : amine Colour : grey-green Density : approx. 1.0 g/ml Viscosity : approx. 2 Pa.s Mixing ratio : A:B 200 : 100
Mixture (Part A+B)
Colour : black Odour : almost without odour Pot life (23°C, 50% rh) : approx. 60 min(s) Initial strength : after 8 hours (23°C, 50% rh) after approx. 15 minutes (80 °C object temperature) Shear strength (based on DIN EN 1465):
- Steel, 0.2 mm thick layer (7 d at 23 °C, 50 % rh) at 23 °C: 25 MPa Peel test (DIN EN ISO 11339):
- Steel, 0.2 mm thick layer (7 d at 23 °C, 50 % rh) : 5 N/mm E-Modulus : >1,300 MPa
Full technical information can be found in technical data sheet
TEROSON EP 5065 is a solvent free, two component adhesive, based on Epoxy resins. It has high final strength both at high and low temperatures (-40°C - 80°C). Curing can be obtained with both low and high temperature. The cured adhesive film is hard, but not brittle.
Application Areas:
TEROSON EP 5065 is mainly used in car repair for structural bonding of metals when requirements in terms of crash behaviors are high (e.g., car body steel with or without e-coat, galvanized steel and aluminum). Coated surfaces are protected against corrosion. Curing can take place at room temperature or be accelerated by the use of additional heat, e.g. IR radiator. The assembly bonded shall be designed so that the bonded surface or seams are only subjected to tensile or shear forces, but not to peel forces. It is recommended that bonding should be done with single overlaps. Uncured adhesive can be spot-welded. Further information about the product: biuro@woronko-kleje.pl
Directions for use:
Pretreatment:
The substrate should be dry, free from dust, oil, grease and other contaminants. An improvement of the adhesion can be achieved by grindings or sandblasting of the surface.
Application:
TEROSON EP 5065 is processed from a 2:1 cartridge. Only use cartridge pistols that are equipped with a piston rod. During the storage time and shipment a crystallization of the resin may occur. By heating the adhesive above 60 °C for about 60 minutes this physical process is reversible. All properties stay afterwards on the same level. It is recommended that the adhesive should be used with a minimum temperature of 15 °C. Prior to screwing the static mixer, a small amount of the material should be pressed out to ensure that both components are passed on simultaneously. Now, the static mixer is screwed onto it. To ensure proper mixing, discard the first approx. 4 cm of the adhesive bead. After mixing, the adhesive is ready for use and must be processed within 1 hour, since viscosity increases when curing starts. The processing time depends on the temperature. In order to avoid the bonded parts being displaced, it is recommended that they should always be fixed.
Curing:
The bonded parts, which have been fixed by means of a slight pressure applied to them, can be cured at room temperature or higher. They can be painted over after having reached their final strength. If suitable equipment for curing at higher temperature (infrared radiator, paint cabin that can be heated to 40 – 80 °C or other equipment) is available, this should always be givenpreference over curing at room temperature for the following reasons:
- Shorter curing time; further processing or treatment is possible after only 2 hours approx.
- Higher strength is achieved
- Higher resistance of the adhesive bond against chemical loads
Cleaning:
Fresh, uncured material can be removed with TEROSON VR 10. Cured adhesive can only be removed mechanically.
Storage:
Parameters:
Part A:
Part B:
Mixture (Part A+B)
- Steel, 0.2 mm thick layer (7 d at 23 °C, 50 % rh) at 23 °C: 25 MPa
- Steel, 0.2 mm thick layer (7 d at 23 °C, 50 % rh) : 5 N/mm
Full technical information can be found in technical data sheet