Product description:
TEROSON EP 5055 is a solvent free, two component adhesive, based on toughened Epoxy resins. The material has a very good adhesion to e.g.:
- bare metal
- aluminum alloys
- zink coated steels
- E-coated panels
By heating up both components the chemical reaction will accelerate. TEROSON EP 5055 will cure at room temperature. Curing can be accelerated by increasing the temperature. It is free of isocyanate and silicones. The cured adhesive film is hard, but not brittle. Further information about the product: biuro@woronko-kleje.pl

Directions for use:
EROSON EP 5055 is processed from universal cartridges with manual application tools (guns driven by hand, air pressure or battery). Only use cartridge pistols that are equipped with a piston rod. Prior to screwing the static mixer, a small amount of the material should be pressed out to ensure that both components are passed on simultaneously. After mixing, the adhesive is ready for use and must be processed within 80 min, since viscosity increases when curing starts. In order to avoid the bonded parts being displaced, it is recommended that they should always be fixed during the process of curing. The processing time depends on the temperature.

Storage:
  • Frost sensitive under certain conditions (may cristalize, reversible > 40 °C)
  • Recommended storage temperature : 15 to 25 °C
  • Shelf life : 12 months in original packaging

    Parameters:
  • Colour : dark grey
  • Odour : almost without odour
  • Solids : 100 %
  • Curing times
    - initial strength approx. 4 h at 23 °C
    - final strength approx. 2 d at 23 °C
  • Shear strength (based on DIN EN 1465)
    - cured at ambient temperature 18 to 22 MPa
    - cured at elevated temperature > 20 MPa
  • Peel test (DIN EN ISO 11339) Steel, 0.2 mm thick layer (7 d at 23 °C, 50 % rh) : >4 N/mm
  • E-Modulus : 1,500 MPa

    Full technical information can be found in the technical data sheet.