LOCTITE AA F 246 + Aktywator INI 5 - 50ml (klej + aktywator)
Nr
IDH.1290612
Cena
185,58 PLN netto
/ szt.
Product description:
LOCTITE® AA F246™ is a two component toughened acrylic adhesive system for high strength structural bonding. It cures rapidly at room temperature on assembly of the joint. Further information about the product: biuro@woronko-kleje.pl
Directions for use:
1. For best performance bond surfaces should be clean and free from grease. You can use for example LOCTITE SF 7063.
2. To ensure a fast and reliable cure, Activator Ini No.1™ or Ini No.5™ should be applied to one of the bond surfaces and the adhesive to the other surface. Parts should be assembled within 15 minutes.
3. The recommended bondline gap is 0.1 mm. Where bond gaps are large (up to a maximum of 0.5 mm), or faster cure speed is required, Activator Ini No.1™ or Ini No.5™ should be applied to both surfaces. Parts should be assembled immediately (within 1 minute).
4. Excess adhesive can be wiped away with organic solvent.
5. Bond should be held clamped until adhesive has fixtured.
6. Product should be allowed to develop full strength before subjecting to any service loads (typically 24 to 72 hours after assembly, depending on bond gap, materials and ambient conditions).
Storage:
Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties Material removed from containers may be contaminated during use. Do not return product to the original container. Henkel Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated.
Parameters:
After 168 hours at 22 °C, Activator Ini No.5™ on 1 sideLap Shear Strength, ISO 4587:
- Grit Blasted Mild Steel (GBMS) N/mm² : 33
- Stainless steel N/mm² : 16
- Aluminum, N/mm² : 19
- ABS, N/mm² : 6.1
- PVC, N/mm² : 11
- Polycarbonate, N/mm² : 4.6
- PMMA, N/mm² : 5.1
Further information can be found in the technical data sheet
LOCTITE® AA F246™ is a two component toughened acrylic adhesive system for high strength structural bonding. It cures rapidly at room temperature on assembly of the joint. Further information about the product: biuro@woronko-kleje.pl
Directions for use:
1. For best performance bond surfaces should be clean and free from grease. You can use for example LOCTITE SF 7063.
2. To ensure a fast and reliable cure, Activator Ini No.1™ or Ini No.5™ should be applied to one of the bond surfaces and the adhesive to the other surface. Parts should be assembled within 15 minutes.
3. The recommended bondline gap is 0.1 mm. Where bond gaps are large (up to a maximum of 0.5 mm), or faster cure speed is required, Activator Ini No.1™ or Ini No.5™ should be applied to both surfaces. Parts should be assembled immediately (within 1 minute).
4. Excess adhesive can be wiped away with organic solvent.
5. Bond should be held clamped until adhesive has fixtured.
6. Product should be allowed to develop full strength before subjecting to any service loads (typically 24 to 72 hours after assembly, depending on bond gap, materials and ambient conditions).
Storage:
Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties Material removed from containers may be contaminated during use. Do not return product to the original container. Henkel Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated.
Parameters:
After 168 hours at 22 °C, Activator Ini No.5™ on 1 side
- Grit Blasted Mild Steel (GBMS) N/mm² : 33
- Stainless steel N/mm² : 16
- Aluminum, N/mm² : 19
- ABS, N/mm² : 6.1
- PVC, N/mm² : 11
- Polycarbonate, N/mm² : 4.6
- PMMA, N/mm² : 5.1
Further information can be found in the technical data sheet