LOCTITE EA M-121HP - 50ml (żywica epoksydowa)

LOCTITE EA M-121HP - 50ml (żywica epoksydowa) (IDH.235033)

Product description:
LOCTITE® EA M-121HP™ is a non-sagging epoxy adhesive which cures at room temperature once mixed, to form a tough, amber-beige bondline with excellent resistance to peel and impact forces. When fully cured, the epoxy offers superior thermal shock resistance, excellent mechanical and electrical properties, and withstands exposure to a wide variety of solvents and chemicals. Typical applications include low stress applications which require high impact and high peel strength. Bonds dissimilar materials including aluminum, steel, and other metals, as well as a variety of plastics and ceramics. Suitable for use in the assembly of disposable medical devices. Further information about the product: biuro@woronko-kleje.pl
Directions for use:
1. For high strength structural bonds, remove surface contaminants such as paint, oxide films, oils, dust, mold release agents and all other surface contaminants.
2. Use gloves to minimize skin contact. DO NOT use solvents for cleaning hands.
3. Dual Cartridges: To use simply insert the cartridge into the application gun and start the plunger into the cylinders using light pressure on the trigger. Next, remove the cartridge cap and expel a small amount of adhesive to be sure both sides are flowing evenly and freely. If automatic mixing of resin and hardener is desired, attach the mixing nozzle to the end of the cartridge and begin dispensing the adhesive. For hand mixing, expel the desired amount of the adhesive and mix thoroughly. Mix for approximately 15 seconds after uniform color is obtained.
4. For maximum bond strength apply adhesive evenly to both surfaces to be joined.
5. Application to the substrates should be made within 2 hours. Larger quantities and/or higher temperatures will reduce this working time.
6. Join the adhesive coated surfaces and allow to cure at 25 °C for 24 hours for high strength. Heat up to 93 °C, will speed curing.
7. Keep parts from moving during cure. Contact pressure is neccesary. Maximum shear strength is obtained with a 0.1 to 0.2 mm bond line.
8. Excessive uncured adhesive can be cleaned up with ketone type solvents
Storage:
Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container. Henkel Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated.
Parameters:
  • Lap Shear Strength, ISO 4587 (Cured at 65 °C for 2 hours):
    - Aluminum (etched & abraded), 0.13 mm N/mm² : ≥13.8
  • Lap Shear Strength, ISO 4587 (Cured at 65 °C for 12 hours):
    - Steel (grit blasted), N/mm² : 29.4
    - Aluminum (etched & abraded), 0.1 to 0.2 mm gap, N/mm² : 33.1
    -Aluminum (anodised), N/mm² : 14.6
    -Stainless steel, N/mm² : 23.1
    -Polycarbonate, N/mm² : 7.0
    -Nylon, N/mm² : 2.3
    -Wood (Fir), N/mm² : 11.3
  • Block Shear Strength, ISO 13445:
    - PVC, N/mm² : 11.7
    - ABS, N/mm² : 7.5
    - Epoxyglass, N/mm² : 20.1
    - Acrylic, N/mm² : 1.5
    - Glass, N/mm² : 22.7

    Full technical information can be found in the technical data sheet